超超臨界機(jī)組HR3C再熱器受熱面管組織、性能及持久壽命分析

打開文本圖片集

文章編號(hào)：2096-2983（2025）03-0086-07

關(guān)鍵詞：HR3C鋼；顯微組織；性能；持久壽命中圖分類號(hào)：TG142.73 文獻(xiàn)標(biāo)志碼：A

Abstract： HR3C，an optimized variant of TP31O austenitic heat-resistant steel， is widely used in supercritical units and ultra-supercritical units because of its good high temperature mechanical properties and high temperature oxidation resistance.The HR3C heating surface tube at the outlet from the final reheater in an ultra-supercritical unit of a power plant with accumulated service of about 60000h （204號(hào) has been taken as the research object. The microstructures and properties as well as creep rupture life were investigated by Brinell hardness tests， tensile tests， metallographic examination， scanning electron microscope and transmission electron microscope observations， and high temperature lasting strength test.The results show that， compared with the as-received state，the amount of precipitated phases in the microstructure of the HR3C heating surface tube after service increases significantly; the Brinell hardnes，the tensile strength and the yield strength all increased，while the plasticity significantly decreases during tensile tests at room temperature，but remains relatively high during tensile tests at high temperatures. Based on the results of the high temperature lasting strength test， the remaining life of the heating surface tube under the service condition of 650°C is calculated to be greater than 100000h

Keywords： HR3C steel; microstructure; properties; creep rupture life

超超臨界（ultra-supercritical，USC）機(jī)組由于具有能源利用率高、排放污染物少等優(yōu)點(diǎn)，是目前火電機(jī)組主要的發(fā)展方向[1]。（剩余7341字）